Hollow latex particles as submicrometer reactors for polymerization in confined geometries

A method was developed for free‐radical polymerization in the confines of a hollow latex particle. Hollow particles were prepared via the dynamic swelling method from polystyrene seed and divinylbenzene and had hollows of 500–1000 nm. So that these hollow poly(divinylbenzene) particles could function as submicrometer reactors, the particles were filled with a monomer (N‐isopropylacrylamide) via the dispersion of the dried particles in the molten monomer. The monomer that was not contained in the hollows was removed by washing and gentle abrasion. Free‐radical polymerization was then initiated by γ radiolysis in the solid state. Transmission electron microscopy showed that poly(N‐isopropylacrylamide) formed in the hollow interior of the particles, which functioned as submicrometer reactors. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5706–5713, 2004     

Polyelectrolyte complexes. VI. Polycation structure,polyanion molar mass,and polyion concentration effects on complex nanoparticles based on poly(sodium 2‐acrylamido‐2‐methylpropanesulfonate)

The formation and characterization of some interpolyelectrolyte complex (IPEC) nanoparticles based on poly(sodium 2‐acrylamido‐2‐methylpropanesulfonate) (NaPAMPS), as a function of the polycation structure, polyanion molar mass, and polyion concentration, were followed in this work. Poly(diallyldimethylammonium chloride) and two polycations (PCs) containing (N,N‐dimethyl‐2‐hydroxypropyleneammonium chloride) units in the backbone (PCA₅ and PCA₅D₁) were used as starting polyions. The complex stoichiometry, (n^?/n⁺)_iso, was pointed out by optical density at 500 nm (OD₅₀₀), polyelectrolyte titration, and dynamic light scattering. IPEC nanoparticle sizes were influenced by the polycation structure and polyanion molar mass only before the complex stoichiometry, which was higher for the more hydrophilic polycations (PCA₅ and PCA₅D₁) and for a higher NaPAMPS molar mass, and were almost independent of these factors after that, at a flow rate of the added polyion of about 0.28 mL × (mL PC)^?1 × h^?1. The IPEC nanoparticle sizes remained almost constant for more than 2 weeks, both before and after the complex stoichiometry, at low concentrations of polyions. NIPECs as stable colloidal dispersions with positive charges in excess were prepared at a ratio between charges (n^?/n⁺) of 0.7, and their storage colloidal stability, as a function of the polycation structure and polyion concentration (from 0.8 to ca. 7.8 mmol/L), was demonstrated. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2495–2505, 2004     

Block copolymer nanoparticles of controlled sizes via ring‐opening metathesis polymerization

This article describes the formation and characterization of self‐assembled nanoparticles of controlled sizes based on amphiphilic block copolymers synthesized by ring‐opening metathesis polymerization. We synthesized a novel hydrophobic derivative of norbornene; this monomer could be polymerized using Grubbs' catalyst [Cl₂Ru(CHPh)(PCy₃)₂] forming polymers of controlled molecular weight. We synthesized amphiphilic block copolymers of controlled composition and showed that they assemble into nanoparticles of controlled size. The nanoparticles were characterized using dynamic light scattering and transmission electron microscopy. Tuning the composition of the block copolymer enables the tuning of the diameters of the nanoparticles in the 30‐ to 80‐nm range. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 3352–3359, 2004     

Metallo‐supramolecular block copolymer micelles: Improved preparation and characterization

Micelles prepared from amphiphilic block copolymers in which a poly(styrene) segment is connected to a poly(ethylene oxide) block via a bis‐(2,2′:6′,2″‐terpyridine‐ruthenium) complex have been intensely studied. In most cases, the micelle populations were found to be strongly heterogeneous in size because of massive micelle/micelle aggregation. In the study reported in this article we tried to improve the homogeneity of the micelle population. The variant preparation procedure developed, which is described here, was used to prepare two “protomer”‐type micelles: PS₂₀‐[Ru]‐PEO₇₀ and PS₂₀‐[Ru]‐PEO₃₇₅. The dropwise addition of water to a solution of the compounds in dimethylformamide was replaced by the controlled addition of water by a syringe pump. The resulting micelles were characterized by sedimentation velocity and sedimentation equilibrium analyses in an analytical ultracentrifuge and by transmission electron microscopy of negatively stained samples. Sedimentation analysis showed virtually unimodal size distributions, in contrast to the findings on micelles prepared previously. PS₂₀‐[Ru]‐PEO₇₀ micelles were found to have an average molar mass of 318,000 g/mol (corresponding to 53 protomers per micelle, which is distinctly less than after micelle preparation by the standard method) and an average hydrodynamic diameter (d_h) of 18 nm. For PS₂₀‐[Ru]‐PEO₃₇₅ micelles, the corresponding values were M = 603,000 g/mol (31 protomers per micelle) and d_h = 34 nm. The latter particles were found to be identical to the “equilibrium” micelles prepared in pure water. Both micelle types had a very narrow molar mass distribution but a much broader distribution of s values and thus of hydrodynamic diameters. This indicates a conformational heterogeneity that is stable on the time scale of sedimentation velocity analysis. The findings from electron microscopy were in disagreement with those from the sedimentation analysis both in average micelle diameter and in the width of the distributions, apparently because of imperfections in the staining procedure. The preparation procedure described also may be useful in micelle formation from other types of protomers. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4458–4465, 2004     

Zn(BTZ)2白色有机电致发光材料的合成及其器件制备

以PCl₃为脱水剂,将邻氨基硫酚与水杨酸脱水环化合成出2-(2-羟基苯基)苯并噻唑,并进一步将所得产物与乙酸锌反应合成出2-(2-羟基苯基)苯并噻唑螯合锌(Zn(BTZ)₂)材料。以该配合物作为发光层制备出结构为ITO/PVK:TPD/Zn(BTZ)₂/Al近白色电致发光器件,其色坐标位于白场之内(x=0.242,y=0.359),在驱动电压为16V时,亮度达3200cdm²,对应的量子效率为0.32%。进一步在Zn(BTZ)₂中掺入橙红色染料Rubrene,制成ITO/PVK:TPD/Zn(BTZ)₂:Rubrene/Al结构器件,实现了纯白色发光(色坐标值:x=0.324,y=0.343),非常接近于白色等能点,且量子效率达0.47%。最后对上述器件的发光和电学性能进行了深入的研究和探讨。     

金纳米粒子光学性质中的尺寸和形状效应

纳米尺度的金属及半导体呈现出特殊的光学、电学及磁学性质,采用近年发展起来的离散偶极近似(DDA)的方法,我们分析了金纳米粒子的尺寸及形状对其光学性质的影响。粒子周围介质的影响在文中亦作了分析。计算结果显示,金纳米粒子的等离子体吸收带同时受到粒子尺寸和形状的影响,但来自形状的影响更为明显。与米氏理论及扩展的甘氏理论相比较,DDA方法在粒子尺寸不再远小于入射光波长的时候更准确,并能应用于任何形状的纳米粒子。理论计算与实验结果能较好的吻合。     

Über die Magnetischen Eigenschaften der Cobaltate Na6CoS4, Na6CoSe4 und K6CoS4

Magnetic Properties of the Cobaltates Na₆CoS₄, Na₆CoSe₄, and K₆CoS₄ The alkali metal cobalt chalcogenides Na₆CoS₄, Na₆CoSe₄, and K₆CoS₄ crystallize in the space group P6₃mc with Z = 4. The structure is characterized by isolated [CoX₄]-tetrahedra. The magnetic susceptibilities show Curie-Weiss behaviour. The deviations at low temperatures are caused by antiferromagnetic interactions. The magnetic moments are discussed with regard to ligand-field parameters.     

Aqueous solution and solid state interactions of lanthanide ions with a methacrylic ester polymer bearing pendant 15‐crown‐5 moieties

The interaction between trivalent lanthanide ions and poly(1,4,7,10,13‐pentaoxacyclopentadecan‐2‐yl‐methyl methacrylate), PCR5, in aqueous solution and in the solid state have been studied. In aqueous solution, evidence of a weak interaction between the lanthanides and PCR5 comes from the small red shift of the Ce(III) emission spectra and the slight broadening of the Gd(III) EPR spectra. From the Tb(III) lifetimes in the presence of H₂O and D₂O the loss of one or two water coordinated molecules is confirmed when Tb(III) is bound to PCR5. An association constant of the order of 200 M^?1 was obtained for a 1:1 (lanthanide:15‐crown‐5) complex from the shift of the polymer NMR signals induced by Tb(III). A similar association constant is obtained from the differences of the molar conductivity of Ce(III) solution at various concentrations in presence and absence of PCR5. When Tb(III) is adsorbed on PCR5 membranes, lifetime experiments in H₂O and D₂O confirm the loss of 5 or 6 water coordinated molecules indicating that in solid state the lanthanide(III)‐PCR5 interaction is stronger than in solution. The adsorption of Ce(III) in PCR5 membranes shows a Langmuir type isotherm, from which an equilibrium constant of 39 M^?1 has been calculated. SEM shows that the membrane morphology is not much affected by lanthanide adsorption. Support for lanthanide ion–crown interactions comes from ab initio calculations on 15‐crown‐5/La(III) complex. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 1788–1799, 2007     

Nano-electrochemical detection of hydrogen or protons using palladium nanoparticles: distinguishing surface and bulk hydrogen.

The benefits of using nanoparticle-modified electrodes are exemplified through the electrochemical detection of protons and/or hydrogen. It is shown that a palladium-nanoparticle-modified boron-doped diamond allows voltammetric information relating to the relative roles played by the surface and the bulk metal to be obtained for the proton-hydrogen system at palladium surfaces which is not accessible using palladium macroelectrodes or microelectrodes.